Standard for Temper:
code |
Chinese Stardard |
Japaness Standard |
American Standard |
European Standard |
|
GB/T 2520-2000 |
JIS G3303-2008 |
ASTM A623M-2002 |
DIN EN 10202-2001 |
T1 |
T1 |
T1 |
T1(T49) |
TS230 |
T-1.5 |
T-1.5 |
- |
- |
- |
T-2 |
T-2 |
T-2 |
T-2(53) |
TS245 |
T-2.5 |
T-2.5 |
T-2.5 |
|
TS260 |
T-3 |
T-3 |
T-3 |
T-3(T57) |
TS275 |
T-3.5 |
T-3.5 |
- |
- |
TS290 |
T-4 |
T-4 |
T-4 |
T-4(T61) |
TH415 |
T-5 |
T-5 |
T-5 |
T-5(T65) |
TH435 |
DR-7M |
DR-7M |
- |
DR-7.5 |
TH520 |
DR-8 |
DR-8 |
DR-8 |
DR-8 |
TH550 |
DR-8M |
DR-8M |
- |
DR-8.5 |
TH580 |
DR-9 |
DR-9 |
DR-9 |
DR-9 |
TH620 |
DR-9M |
DR-9M |
DR-9M |
DR-9.5 |
- |
DR-10 |
DR-10 |
DR-10 |
- |
- |
Surface state of tinplate:
Marks |
Surface state |
Nominal Surface Roughness Ra)μm |
Characteristics |
B |
Bright rough |
≤0.35 |
Glazed surface obtained after melting treatment of electrotinned smooth raw material strip featuring certain oriented rubstone figure. |
R |
Stone rough |
0.25-0.60 |
Glazed surface obtained after melting treatment of electrotinned raw material strip featuring certain oriented rubstone figure. |
S |
Silver rough |
0.5-1.00 |
Glazed surface obtained after melting treatment of electrotinned raw material strip with rough matt surface. |
M |
Matte rough |
0.80-2.50 |
Matt surface of general matt raw material strip without melting treatment |
Coating weight:
Classification |
Designation of Tin Coating Weight |
Min./Average Tin Coat weight(g/m2) |
Former Coating Designation |
Equal Tin Coating |
1.4/1.4 |
1.2/1.2 |
#15 |
2.2/2.2 |
2.0/2.0 |
#20 |
2.8/2.8 |
2.45/2.45 |
#25 |
5.6/5.6 |
5.05/5.05 |
#50 |
8.4/8.4 |
7.55/7.55 |
#75 |
11.2/11.2 |
10.1/10.1 |
#100 |
Differentially Coated |
1.4/2.8 |
1.2/2.45 |
#15/25 |
2.2/2.8 |
2.2/2.45 |
#20/25 |
2.8/5.6 |
2.45/5.05 |
#25/50 |
2.8/8.4 |
2.45/7.55 |
#25/75 |
2.8/11.2 |
2.45/10.1 |
#25/100 |
5.6/8.4 |
5.05/7.55 |
#50/75 |
5.6/11.2 |
5.05/10.1 |
#50/100 |
8.4/11.2 |
7.55/10.1 |
#75/100 |
|
|